JS-1184CC
Silicone potting adhesive
Silicone potting adhesive
JS-1184CC is a transparent condensation type two component silicone sealant, used in a 10:1 weight ratio. The product does not release heat during curing, has no corrosion, and has a fast curing speed. After curing, it has good transparency, resistance to high and low temperatures, aging, and other characteristics.
Product parameters
| Project | Component A | Component B | Testing standards |
|---|---|---|---|
| Appearance | Transparent liquid | Transparent liquid | Visualization |
| Viscosity (mPa·s) | 1200~1800 | 1200~1800 | GB/T 2794 |
| Component A: Component B (weight ratio) | 10:1 | 10:1 | / |
| Specific gravity after mixing (g/cm3) | 0.97 | 0.97 | GB/T 13477-2002 |
| Operable time ( min/25°C ) | 50-80 | 50-80 | / |
| Complete curing time ( h/25°C ) | 24 | 24 | / |
| Hardness after curing (Shore A) | 15~40 | 15~40 | GB/T 531-2008 |
| Breakdown voltage(kV/mm) | 18 | 18 | / |
| Volume resistivity(Ω·cm) | 2.0x1014 | 2.0x1014 | GB/T 1692 |
| Dielectric loss(1MHz) | 0.002 | 0.002 | GB/T 1693 |
| Operating temperature range (°C ) | -40~180 | -40~180 | / |
Note: The above performance was measured after 7 days of curing under standard environmental conditions (23 ± 2 ° C, 50 ± 5 ° C).
Operation and Safety
- 1. Clean the dust, oil, etc. on the sealing surface before use.
- 2. When mixing, the weight ratio of component A to component B=10:1 should be followed.
- 3. Mix component A and component B evenly, and avoid high-speed and prolonged mixing to prevent shortened operation time and accelerated solidification. After stirring evenly, it can be left to stand for deaeration or vacuum deaeration.
Color and packaging
This product is packaged in 10L plastic barrels and 1L plastic kettles, or other specifications may be agreed upon.
Storage and expiration date
This product belongs to non hazardous materials and should be stored in a cool and dry place at a storage temperature below 30 ° C.
The storage period is 6 months.
Data download